Material of alignment films, methods of fabricating liquid crystal display panels and liquid crystal display panels

ABSTRACT

The present application provides a material of alignment film, a method of fabricating a liquid crystal display panel, and a liquid crystal display panel. The material of alignment film of the present application is obtained by mixing a polymerizable monomer in the polyamic acid solution, thus is easy to fabricate. The method of fabricating the liquid crystal display panel of the present application obtains an alignment film including a polyimide film and polymer protrusions located on a surface of the polyimide film by coating the material of alignment film on a substrate, and going through a series of processes; the alignment film can allow liquid crystal molecules arrange in vertical alignment and generate a pre-inclination angle, and a risk of the polymerizable monomer contaminating the liquid crystal molecules does not exist, so as to enhance quality of the liquid crystal display panel. The liquid crystal display panel of the present application has a simple structure and good alignment effect, and has excellent display quality.

FIELD OF THE INVENTION

The present application relates to display technical field, especiallyto a material of alignment film, a method of fabricating a liquidcrystal display panel, and a liquid crystal display panel.

BACKGROUND OF THE INVENTION

With the development of display technology, a liquid crystal display(LCD) device has many advantages of high definition, power saving, thinbody, and wide application, so it is widely used in a variety ofconsumer electronic products such as mobile phones, televisions (TV),personal digital assistants, digital cameras, notebook computers,desktop computers etc., and becomes the main stream in the displaydevices.

Most of the liquid crystal devices in current market are the backlighttype liquid crystal display, which includes a liquid crystal displaypanel and a backlight module. The working principle of the liquidcrystal display panel is: placing liquid crystal molecules in twoparallel glass substrates, which have many vertical and horizontal finewires between the two glass substrates; controlling the liquid crystalmolecules to change direction by energizing or not energizing; andrefracting light of the backlight module to produce frames.

Generally, the liquid crystal display panel is consisting of a colorfilter (CF) substrate, a thin film transistor (TFT) substrate, liquidcrystal (LC) interposed between the CF substrate and the TFT substrate,and a sealant.

In TFT-LCD, vertically aligned (VA) becomes a common mode of large-sizeTVs, with its advantages of wide viewing angle, high contrast, and noneed of friction alignment. The VA techniques are mainly divided intomulti-domain vertical alignment (MVA) technique, patterned verticalalignment (PVA) technique, and continuous pinwheel alignment (CPA)technique. Such the VA techniques all are needed to design protrusionsor slits on the CF side, at the same time of increasing cost, lighttransmittance of the display screens are also reduced, to solve aproblem of implementing a plane control of the CF side from the point orline control, a new VA display technique, called polymer stabilizationvertical alignment (PSVA) technique, is produced.

The greatest feature of polymer stabilization vertical alignmenttechnique is that a polymer layer, which can allow vertical alignmentliquid crystal form a pre-inclination angle, is formed on the alignmentfilm, a formation of this polymer film is shown in FIGS. 1A to 1D, asshown in FIG. 1A, a certain ratio of high purity reactive mesogen (RM)200 is blended in liquid crystal molecules 100, this is a phototropismmonomer containing a double bond; as shown in FIG. 1B, beforeultraviolet (UV) irradiation, an external voltage is applied to a uppersubstrate 300 and a lower substrate 100, to allow the liquid crystalmolecules generate a pre-inclination angle, corresponding to differentdomains, inclination directions of the liquid crystal molecules 100 aredifferent; as shown in FIG. 1C, after the pre-inclination angle isdetermined with the external voltage, performing a specific UVirradiation, at this time, the reactive mesogen 200 polymerizes to forma polymer network 500 that attracts the liquid crystal molecules 100 toform a fixed pre-inclination angle; as shown in FIG. 1D, after the UVirradiation is completed and the external voltage is removed, the liquidcrystal molecules 100 on surfaces of the upper substrate 300 and thelower substrate 400 still keep at the certain pre-inclination angle.

However, after the reactive mesogen occurs the free radicalpolymerization under the UV irradiation, there will be more or less thereactive mesogen left in the liquid crystal; thus contaminating theliquid crystal, resulting in presence of ghost, and reducing quality ofthe panel.

SUMMARY OF THE INVENTION

A primary aspect of the present application is to provide a material ofalignment film, which can simplify the liquid crystal alignment process,does not contaminate the liquid crystal, and enhances quality of liquidcrystal display panel.

Another aspect of the present application is to provide a method offabricating a liquid crystal display panel, which can achieve verticalalignment of the liquid crystal molecules and generate a pre-inclinationangle thereof, a risk of the polymerizable monomer contaminating theliquid crystal molecules does not exist, and the quality of liquidcrystal display panel is enhanced.

A further aspect of the present application is to provide a liquidcrystal display panel, which has a simple structure and good alignmenteffect, and has excellent display quality.

To achieve the aforesaid aspects, the present application firstlyprovides a material of alignment film including a polyamic acidcontaining aromatic fused ring structure, a polymerizable monomercontaining aromatic fused ring structure, and a solvent;

the polyamic acid containing aromatic fused ring structure including:one or more than one in

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing a cyclic unit;

the polymerizable monomer containing aromatic fused ring structureincludes one or more than one in

wherein P represents the polymerizable group, which is selected from atleast one of methacrylate group, acrylate group, vinyl, ethyleneoxy, andepoxy; n is a number of the polymerizable group connecting to the samearomatic ring, n=1, 2 or 3, when n is greater than 1, the npolymerizable groups P are the same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2˜8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

A mass percentage of the polyamic acid containing aromatic fused ringstructure is 3˜4%, a mass percentage of the polymerizable monomercontaining aromatic fused ring structure is 0.03˜0.4%, a mass percentageof the solvent is 95.6˜96.97%.

The polyamic acid containing aromatic fused ring structure includes

the polymerizable monomer containing aromatic fused ring structureincludes

The present application further provides a method of fabricating aliquid crystal display panel, including following steps:

step 1, providing a material of alignment film, the material ofalignment film including a polyamic acid containing aromatic fused ringstructure, a polymerizable monomer containing aromatic fused ringstructure, and a solvent;

the polyamic acid containing aromatic fused ring structure including oneor more than one in

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing cyclic unit;

the polymerizable monomer containing aromatic fused ring structureincludes one or more than one in

wherein P represents the polymerizable group, which is selected from atleast one of methacrylate group, acrylate group, vinyl, ethyleneoxy, andepoxy; n is a number of the polymerizable group connecting to the samearomatic ring, n=1, 2 or 3, when n is greater than 1, the npolymerizable groups P are the same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different;

step 2, providing a first substrate and a second substrate, the firstsubstrate including a first underlying substrate and a first electrodedisposed on the first underlying substrate, the second substrateincluding a second underlying substrate and a second electrode disposedon the second underlying substrate;

coating the material of alignment film provided in step 1 on a surfaceof the first electrode of the first substrate and a surface of thesecond electrode of the second substrate;

baking the material of alignment film, to completely volatilize thesolvent, simultaneously to make dehydration and cyclization of thepolyamic acid containing aromatic fused ring structure, then to beconverted to a polyimide containing aromatic fused ring, to form apolyimide film, and the polyimide film containing a polymerizablemonomer containing aromatic fused ring structure;

step 3, dripping liquid crystal molecules on the surface of the firstsubstrate or second substrate that the polyimide film is disposedthereon, coating a sealant on a periphery corresponding to the liquidcrystal molecules on the side of the second substrate or first substratethat the polyimide film is disposed thereon;

step 4, laminating the first substrate and the second substrate atcorresponding position, so that a liquid crystal layer is formed by theliquid crystal molecules located between the first substrate and thesecond substrate; curing the sealant, at this time, the liquid crystalmolecules arranging perpendicular to the first substrate and the secondsubstrate;

step 5, applying a voltage to both sides of the liquid crystal layerthrough the first electrode and the second electrode, after the liquidcrystal molecules deflected, at the same time of applying the voltage,performing UV irradiation to the polyimide film, to form polymerprotrusions on the surface of the polyimide film by polymerizing thepolymerizable monomer containing aromatic fused ring structure by actionof photo initiation, so that a first alignment film and a secondalignment film are respectively formed on the surfaces of the firstsubstrate and the second substrate, both the first alignment film andthe second alignment film include the polyimide film and the polymerprotrusions located on the surface of the polyimide film;

after the UV irradiation is stopped and the voltage is removed, theliquid crystal molecules near surfaces of the first alignment film andthe second alignment film generates a pre-inclination angle.

In the material of alignment film of step 1, the polyamic acidcontaining aromatic fused ring structure includes

the polymerizable monomer containing aromatic fused ring structureincludes

A mass percentage of the polyamic acid containing aromatic fused ringstructure is 3˜4%, a mass percentage of the polymerizable monomercontaining aromatic fused ring structure is 0.03˜0.4%, a mass percentageof the solvent is 95.6˜96.97%.

The method of preparing the material of alignment film provided in step1 including:

step 11, providing a dianhydride based monomer containing aromatic fusedring structure and a diamine based monomer, dissolving the dianhydridebased monomer containing aromatic fused ring structure and the diaminebased monomer in the solvent, reacting to obtain the polyamic acidcontaining aromatic fused ring structure, so as to obtain a polyamicacid solution;

step 12, providing a polymerizable monomer containing aromatic fusedring structure, adding the polymerizable monomer containing aromaticfused ring structure into the polyamic acid solution obtained in step11, to obtain the material of alignment film.

In step 5, the voltage applied to the both sides of the liquid crystallayer is 13˜25V, an intensity of ultraviolet (UV) during the UVirradiation is 85˜100 mW/cm², an irradiation time is 20˜30 min.

The present application further provides a liquid crystal display panelincluding: oppositely disposed a first substrate and a second substrate,a liquid crystal layer disposed between the first substrate and thesecond substrate, a first alignment film disposed on the first substratenear a side of the liquid crystal layer, and a second alignment filmdisposed on the second substrate near a side of the liquid crystallayer;

both the first alignment film and the second alignment film including apolyimide film and polymer protrusions located on a surface of thepolyimide film;

a material of the polyimide film including a polyimide containingaromatic fused ring structure, the polyimide containing aromatic fusedring structure including one or more than one in

wherein x≥1;

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing cyclic unit;

the polymer protrusions are formed by polymerizing the polymerizablemonomer containing aromatic fused ring structure, the polymerizablemonomer containing aromatic fused ring structure includes one or morethan one in

P represents a polymerizable group, which is selected from at least oneof methacrylate group, acrylate group, vinyl, ethyleneoxy, and epoxy; nis a number of the polymerizable P connecting to the same aromatic ring,n=1, 2, or 3, when n is greater than 1, the n polymerizable groups P arethe same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

The polyimide containing aromatic fused ring structure includes

the polymerizable monomer containing aromatic fused ring structureincludes

Advantages of the present application: The material of alignment film ofthe present application is obtained by mixing a polymerizable monomer inthe polyamic acid solution, thus is easy to fabricate. The method offabricating the liquid crystal display panel of the present applicationobtains an alignment film including a polyimide film and polymerprotrusions located on a surface of the polyimide film by coating thematerial of alignment film on a substrate, and going through a series ofprocesses; the alignment film can allow liquid crystal molecules arrangein vertical alignment and generate a pre-inclination angle, a risk ofthe polymerizable monomer contaminating the liquid crystal moleculesdoes not exist, and quality of the liquid crystal display panel isenhanced. The liquid crystal display panel of the present applicationhas a simple structure and good alignment effect, and has excellentdisplay quality.

BRIEF DESCRIPTION OF THE DRAWINGS

The technical features and other advantages of the present applicationwill become more readily apparent to those ordinarily skilled in theart, by referring the following detailed description of embodiments ofthe present application in conjunction with the accompanying drawings.

In the accompanying drawings,

FIGS. 1A-1D schematically illustrate a process of current polymervertical alignment technique;

FIG. 2 is a flowchart of a method of fabricating a liquid crystaldisplay panel of the present application;

FIG. 3 schematically illustrates steps 2-4 of the method of fabricatingthe liquid crystal display panel of the present application; and

FIGS. 4-5 schematically illustrate step 5 of the method of fabricatingthe liquid crystal display panel of the present application, and FIG. 5schematically illustrates a structure of a liquid crystal display panelof the present application.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

In order to further clarify the technical means adopted in the presentapplication and the effects thereof, the preferable embodiments of thepresent application and the accompanying drawings thereof will be morespecifically described as follows.

The present application firstly provides a material of alignment filmincluding a polyamic acid containing aromatic fused ring structure, apolymerizable monomer containing aromatic fused ring structure, and asolvent;

the polyamic acid containing aromatic fused ring structure including oneor more than one in

wherein x is 20˜10000;

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing a cyclic unit.

Specifically, the cyclic unit includes one or more than one infive-membered ring and six-membered ring; the six-membered ring includesone or more than one in aromatic ring and aliphatic ring.

Preferably,

includes one or a combination of more than one of

Preferably, the polyamic acid containing aromatic fused ring structureincludes

wherein x is 20˜40000.

The polymerizable monomer containing aromatic fused ring structureincludes one or more than one in

wherein P represents the polymerizable group, which is selected from atleast one of methacrylate group, acrylate group, vinyl, ethyleneoxy, andepoxy; n is a number of the polymerizable group connecting to the samearomatic ring, n=1, 2 or 3, when n is greater than 1, the npolymerizable groups P are the same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

An ordinarily skilled person in the art can understand that n+m must beless than or equal a total number of groups capable of connecting to thesame aromatic ring.

Preferably, the polymerizable monomer containing aromatic fused ringstructure includes

Specifically, the solvent includes one or more than one of N-methylpyrrolidone (NMP), N-ethyl pyrrolidone, γ-caprolactone, dimethylsulfoxide, and methylene chloride. Preferably, the solvent is N-methylpyrrolidone.

Specifically, a mass percentage of the polyamic acid containing aromaticfused ring structure is 3˜4%, a mass percentage of the polymerizablemonomer containing aromatic fused ring structure is 0.03˜0.4%, a masspercentage of the solvent is 95.6˜96.97%.

Please refer to FIG. 2, the present application provides a method offabricating a liquid crystal display panel including following steps.

Step 1, providing a material of alignment film, the material ofalignment film including a polyamic acid containing aromatic fused ringstructure, a polymerizable monomer containing aromatic fused ringstructure, and a solvent.

Specifically, the polyamic acid containing aromatic fused ring structureincluding one or more than one in

wherein x is 20˜10000;

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing cyclic unit.

Specifically, the cyclic unit includes one or more than one infive-membered ring and six-membered ring; the six-membered ring includesone or more than one in aromatic ring and aliphatic ring.

Preferably,

includes one or a combination of more than one of

Specifically, the polymerizable monomer containing aromatic fused ringstructure includes one or more than one in

wherein P represents the polymerizable group, which is selected from atleast one of methacrylate group, acrylate group, vinyl, ethyleneoxy, andepoxy; n is a number of the polymerizable group connecting to the samearomatic ring, n=1, 2 or 3, when n is greater than 1, the npolymerizable groups P are the same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

Specifically, in the material of alignment film, a mass percentage ofthe polyamic acid containing aromatic fused ring structure is 3˜4%, amass percentage of the polymerizable monomer containing aromatic fusedring structure is 0.03˜0.4%, a mass percentage of the solvent is95.6˜96.97%.

Specifically, the method of preparing the material of alignment filmprovided in step 1 including:

step 11, providing a dianhydride based monomer containing aromatic fusedring structure and a diamine based monomer, dissolving the dianhydridebased monomer containing aromatic fused ring structure and the diaminebased monomer in the solvent, reacting to obtain the polyamic acidcontaining aromatic fused ring structure, so as to obtain a polyamicacid solution.

Specifically, in step 11, the dianhydride based monomer containingaromatic fused ring structure and the diamine based monomer aredissolved in the solvent according a molar ratio of 1:1. Specifically,step 11 is performed at room temperature, a reaction is 20˜30 hours,preferable 24 hours.

Specifically, a structural formula of the dianhydride based monomercontaining aromatic fused ring structure is

wherein

includes one or a combination of more than one of

Preferably, the dianhydride based monomer containing aromatic fused ringstructure is

Specifically, the diamine based monomer includes at least one of adiamine based monomer containing aromatic fused ring structure, and adiamine based monomer not containing aromatic fused ring structure.

Specifically, a structural formula of the diamine based monomercontaining aromatic fused ring structure is

wherein

includes one or a combination of more than one of

Preferably, the diamine based monomer containing aromatic fused ringstructure is

Specifically, a structural formula of the diamine based monomer notcontaining aromatic fused ring structure is

wherein

is non-aromatic fused ring based group containing cyclic unit.

Specifically, the cyclic unit includes one or more than one infive-membered ring and six-membered ring; the six-membered ring includesone or more than one in aromatic ring and aliphatic ring.

Preferably,

includes one or a combination of more than one of

Specifically, a reaction formula that the diamine based monomercontaining aromatic fused ring structure

and the diamine based monomer containing aromatic fused ring structure

occur the reaction of forming the polyamic acid containing aromaticfused ring structure is:

the polyamic acid containing aromatic fused ring structure obtained bythe aforesaid reaction is

wherein x is 20˜10000.

Specifically, the solvent includes one or more than one of N-methylpyrrolidone (NMP), N-ethyl pyrrolidone, γ-caprolactone, dimethylsulfoxide, and methylene chloride. Preferably, the solvent is N-methylpyrrolidone.

Step 12, providing a polymerizable monomer containing aromatic fusedring structure, adding the polymerizable monomer containing aromaticfused ring structure into the polyamic acid solution obtained in step11, to obtain the material of alignment film.

Specifically, in step 12, the polymerizable monomer containing aromaticfused ring structure is added in the polyamic acid solution according toa ratio of 0.5˜10% that is a molar ratio of the polymerizable monomercontaining aromatic fused ring structure to the dianhydride basedmonomer containing aromatic fused ring structure or the diamine basedmonomer added in step 11.

Specifically, the polymerizable monomer containing aromatic fused ringstructure includes one or more than one in

wherein P represents the polymerizable group, which is selected from atleast one of methacrylate group, acrylate group, vinyl, ethyleneoxy, andepoxy; n is a number of the polymerizable group connecting to the samearomatic ring, n=1, 2 or 3, when n is greater than 1, the npolymerizable groups P are the same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

Preferably, the polymerizable monomer containing aromatic fused ringstructure includes

In comparison with the methylacrylate based polymerizable monomercontaining benzene ring selected by the conventional vertical alignmenttechnique, the polymerizable monomer containing aromatic fused ringstructure selected by the present application has stronger heatresistance and light reaction ability.

Step 2, please refer to FIG. 3, providing a first substrate 10 and asecond substrate 20, the first substrate 10 including a first underlyingsubstrate 11 and a first electrode 12 disposed on the first underlyingsubstrate 11, the second substrate 20 including a second underlyingsubstrate 21 and a second electrode 22 disposed on the second underlyingsubstrate 21;

coating the material of alignment film provided in step 1 on a surfaceof the first electrode 12 of the first substrate 10 and a surface of thesecond electrode 22 of the second substrate 20;

baking the material of alignment film, to completely volatilize thesolvent, simultaneously to make dehydration and cyclization of thepolyamic acid containing aromatic fused ring structure, then to beconverted to a polyimide containing aromatic fused ring, to form apolyimide film 50, and the polyimide film 50 containing a polymerizablemonomer containing aromatic fused ring structure.

Specifically, in step 2, baking the material of alignment film isperformed under a temperature condition of 180˜200° C.; a baking time is20 min-60 min, preferably is 30 min.

Specifically, the polyimide containing aromatic fused ring structureobtained in step 2 includes including one or more than one in

wherein x is 20˜10000;

wherein include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing cyclic unit.

Specifically, the cyclic unit includes one or more than one infive-membered ring and six-membered ring; the six-membered ring includesone or more than one in aromatic ring and aliphatic ring.

Preferably,

includes one or a combination of more than one of

Preferably, a reaction formula of dehydrating and converting thepolyamic acid containing aromatic fused ring structure

to a polyimide containing aromatic fused ring is:

The polyimide containing aromatic fused ring structure obtained by theaforesaid reaction is

wherein x is 20˜10000.

By introducing the group A containing aromatic fused ring structure inthe polyimide, light absorbing ability of the polyimide film 50 can bestrengthened, ability of controlling the polymerizable monomer isincreased, and heat resistance of the polyimide film 50 is alsoincreased.

Due polarity of the polyimide containing aromatic fused ring structureis stronger than polarity of the polymerizable monomer containingaromatic fused ring structure, the two will produce phase separation,the polymerizable monomer containing aromatic fused ring structure tendsto concentrate on the surface of the polyimide film 50.

Step 3, please refer to FIG. 3, dripping liquid crystal molecules on thesurface of the first substrate 10 or second substrate 20 that thepolyimide film 50 is disposed thereon, coating a sealant 40 on aperiphery corresponding to the liquid crystal molecules on the side ofthe second substrate 20 or first substrate 10 that the polyimide film 50is disposed thereon.

Preferably, step 3 further includes coating a conductive adhesive on aperiphery corresponding to the sealant 40 on the side of the secondsubstrate 20 or first substrate 10.

Step 4, please refer to FIG. 3, laminating the first substrate 10 andthe second substrate 20 at corresponding position, so that a liquidcrystal layer 30 is formed by the liquid crystal molecules locatedbetween the first substrate 10 and the second substrate 20; curing thesealant 40, at this time, the liquid crystal molecules arrangingperpendicular to the first substrate 10 and the second substrate 20.

Specifically, in step 4, laminating the first substrate 10 and thesecond substrate 20 at corresponding position is performed under avacuum environment.

Specifically, in step 4, the method of curing the sealant 40 includesone or more than one of thermal curing or UV curing.

Step 5, please refer to FIGS. 4-5, applying a voltage to both sides ofthe liquid crystal layer 30 through the first electrode 12 and thesecond electrode 22, after the liquid crystal molecules deflected, atthe same time of applying the voltage, performing UV irradiation to thepolyimide film 50, to form polymer protrusions 60 on the surface of thepolyimide film 50 by polymerizing the polymerizable monomer containingaromatic fused ring structure by action of photo initiation, so that afirst alignment film 61 and a second alignment film 62 are respectivelyformed on the surfaces of the first substrate 10 and the secondsubstrate 20, both the first alignment film 61 and the second alignmentfilm 62 include the polyimide film 50 and the polymer protrusions 60located on the surface of the polyimide film 50;

after the UV irradiation is stopped and the voltage is removed, theliquid crystal molecules near surfaces of the first alignment film 61and the second alignment film 62 generates a pre-inclination angle.

Specifically, in step 5, the polymer protrusions 60 play a role ofmaintaining the deflection angle of the liquid crystal molecules on thesurfaces of the first alignment film 61 and the second alignment film62.

Specifically, in step 5, the voltage applied to the both sides of theliquid crystal layer 30 is 13˜25V, an intensity of ultraviolet (UV)during the UV irradiation is 85˜100 mW/cm², an irradiation time is 20˜30min.

Specifically, in step 5, the pre-inclination angle of the liquid crystalmolecules is 0.5°˜2°.

In the method of fabricating the liquid crystal display panel of thepresent application, a material of alignment film is obtained by mixinga polymerizable monomer in polyamic acid solution, a polyimide filmcontaining polymerizable monomer containing aromatic fused ringstructure is obtained by coating and baking the material of alignmentfilm on a substrate, after UV irradiates the polyimide film, polymerprotrusions on the polyimide film are formed by polymerizing thepolymerizable monomer, the liquid crystal molecules generate thepre-inclination angle under coordination of the voltage, so as toachieve alignment effect, in comparison with polymer vertical alignmenttechnique, the present application does not need to mix polymerizablemonomer in liquid crystal molecules, the residual polymerizable monomercontaminating the liquid crystal molecules after the UV reaction can beobviated, and quality of the liquid crystal display panel is enhanced.

Please refer to FIG. 5, based on the aforesaid method of fabricating theliquid crystal display panel, The present application further provides aliquid crystal display panel including: oppositely disposed a firstsubstrate 10 and a second substrate 20, a liquid crystal layer 30disposed between the first substrate 10 and the second substrate 20, afirst alignment film 61 disposed on the first substrate 10 near a sideof the liquid crystal layer 30, and a second alignment 62 film disposedon the second substrate 20 near a side of the liquid crystal layer 30;

both the first alignment film 61 and the second alignment film 62including a polyimide film 50 and polymer protrusions 60 located on asurface of the polyimide film 50;

a material of the polyimide film including a polyimide containingaromatic fused ring structure, the polyimide containing aromatic fusedring structure including one or more than one in

wherein x is 20˜10000;

wherein

include one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing cyclic unit.

Specifically, the cyclic unit includes one or more than one infive-membered ring and six-membered ring; the six-membered ring includesone or more than one in aromatic ring and aliphatic ring.

Preferably,

includes one or a combination of more than one of

Preferably, the polyimide containing aromatic fused ring structureincludes

By introducing the group

containing aromatic fused ring structure in the polyimide, lightabsorbing ability of the polyimide film 50 can be strengthened, abilityof controlling the polymerizable monomer is increased, and heatresistance of the polyimide film 50 is also increased.

The polymer protrusions are formed by polymerizing the polymerizablemonomer containing aromatic fused ring structure, the polymerizablemonomer containing aromatic fused ring structure includes one or morethan one in

P represents a polymerizable group, which is selected from at least oneof methacrylate group, acrylate group, vinyl, ethyleneoxy, and epoxy; nis a number of the polymerizable P connecting to the same aromatic ring,n=1, 2, or 3, when n is greater than 1, the n polymerizable groups P arethe same or different;

X represents a substituent, which is selected from at least one of —F,—Cl, —Br, methyl, —CN, straight or branched chain alkyl of 2-8 carbonatoms, and a group obtained by substituting one or more than one methylin the alkyl with oxygen or sulfur atom; m is a number of thesubstituent X connecting to the same aromatic ring, m=1, 2 or 3, when mis greater than 1, the m substituents X are the same or different.

Preferably, the polymerizable monomer containing aromatic fused ringstructure includes

By introducing the aromatic fused ring structure in the polymerizablemonomer, heat resistance of the polymerizable monomer can be enhanced;simultaneously, light reaction ability of the polymerizable isincreased.

Specifically, the first substrate 10 includes a first underlyingsubstrate 11 and a first electrode 12 disposed between the firstunderlying substrate 11 and the first alignment film 61, the secondsubstrate 20 includes a second underlying substrate 21 and a secondelectrode 22 disposed between the second underlying substrate 21 and thesecond alignment film 62.

Specifically, the liquid crystal display panel further includes asealant 40 disposed between the first substrate 10 and the secondsubstrate 20, and located on a periphery of the liquid crystal layer 30.

Preferably, the liquid crystal display panel further includes aconductive adhesive disposed between the first substrate 10 and thesecond substrate 20, and located on a periphery of the sealant 40.

The liquid crystal display panel of the present application has a simplestructure and good alignment effect, and has excellent display quality.

In summary, the present application provides a material of alignmentfilm, a method of fabricating a liquid crystal display panel, and aliquid crystal display panel. The material of alignment film of thepresent application is obtained by mixing a polymerizable monomer in thepolyamic acid solution, thus is easy to fabricate. The method offabricating the liquid crystal display panel of the present applicationobtains an alignment film including a polyimide film and polymerprotrusions located on a surface of the polyimide film by coating thematerial of alignment film on a substrate, and going through a series ofprocesses; the alignment film can allow liquid crystal molecules arrangein vertical alignment and generate a pre-inclination angle, and a riskof the polymerizable monomer contaminating the liquid crystal moleculesdoes not exist, so as to enhance quality of the liquid crystal displaypanel. The liquid crystal display panel of the present application has asimple structure and good alignment effect, and has excellent displayquality.

Based on the above description, an ordinarily skilled in the art cancomplete various similar modifications and arrangements according to thetechnical programs and ideas of the present application, and the scopeof the appended claims of the present application should encompass allsuch modifications and arrangements.

What is claimed is:
 1. A material of alignment film, comprising: apolyamic acid containing aromatic fused ring structure, a polymerizablemonomer containing aromatic fused ring structure, and a solvent; whereinthe polyamic acid containing aromatic fused ring structure comprises:one or more than one in

wherein

comprise one or a combination of more than one of

are the same or different;

is a non-aromatic fused ring based group containing a cyclic unit; andthe polymerizable monomer containing aromatic fused ring structurecomprises


2. The material of alignment film according to claim 1, wherein a masspercentage of the polyamic acid containing aromatic fused ring structureis 3˜4%, a mass percentage of the polymerizable monomer containingaromatic fused ring structure is 0.03˜0.4%, a mass percentage of thesolvent is 95.6˜96.97%.